1. What is laminating?
2. What is the difference between laminating, encapsulating and mounting?
3. Why use cold (pressure sensitive) films?
4. Why use hot (heat activated) films?
5. Why use water-based adhesives?
6. Why use solvent-based adhesives?
7. Why use hot melt adhesives?
8. Why use polyester films?
9. Why use PVC films?
10. Why use TedlarŽ films?
11. What is Laking?
12. What is Piping?
13. What is Silvering?
14. What is Telescoping?
15. What is Shrinkage?
16. How do you know if your adhesive is water-based or not?
17. What is Curling?
18. What is Boat waking?
19. Why is my laminate not sticking to the image?
20. How long will my print last if I laminate it with a UV protective laminating film?
21. Can I roll up a print if it is laminated with a pressure sensitive film and will it “tunnel”?
22. Are SEAL adhesives “archival?”
23. What is a high temperature heat activated film and a low temperature heat activated film?
24. Can I use the least expensive heat activated film for all lamination?
25. What is a release liner?
26. What is the ‘film to adhesive ratio’ and what is its relevance?
27. What is a Decal?

1. What is laminating?
Laminating is a finishing method in which a "film" is applied to the face of a printed graphic. Laminating can provide color enhancement, durability, variety of finishes, and reflective qualities of a printed graphic. Some films will also provide protection from UV rays, along with adding value and longevity to your graphic.

Top

2. What is the difference between laminating, encapsulating and mounting?
Laminating is adding protection or a desired look to a print. Encapsulation is sealing the print above and below with a heat activated laminate. Mounting is applying an image to a rigid substrate.

Top

3. Why use cold (pressure sensitive) films?
If an image or printed media is sensitive to heat or the surface has adhesion problems, it is preferable to use pressure sensitive films. Generally films and adhesives for long term outdoor use are pressure sensitive.

Top

4. Why use hot (heat activated) films?
Heat activated films form a better and more permanent bond to suitable material surfaces and are generally less expensive than pressure-sensitive films.

Top

5. Why use water-based adhesives?
Advantages of water based adhesives:
- Lower cost solution than solvent
- Suitable for both lamination and adhesive films

Top

6. Why use solvent-based adhesives?
Advantages of solvent based adhesives:
- Suitable for outdoor use and long term applications
- Can include high level of UV protection into adhesive
- Suitable for both lamination and adhesive films
- The high tack qualities of the adhesive are good for low surface energy substrates such as polystyrene.

Top

7. Why use hot melt adhesives?
Advantages of Hotmelt Adhesives:
- Not affected by moisture in application
- Low cost
- Short term outdoor use
- High adhesion

Top

8. Why use polyester films?
Polyester films are durable dimensionally stable films that are generally used for gloss lamination films as they are able to achieve the highest gloss level available.

Polyester films have a high melting point. Watch out for UV protection levels if required.

Top

9. Why use PVC films?
PVC (vinyl) based films are best suited for top coating vinyl medias and substrates. They will provide similar rates of expansion/contraction to the media they are applied to. Some vinyl based films offer high levels of UV protection (Print-Guard UV).

Top

10. Why use TedlarŽ films?
A TedlarŽ PVF film is strong, flexible, and fatigue-resistant. Its resistance to failure by flexing is outstanding. TedlarŽ performs well in temperatures ranging from approximately 72 to 107°C (98 to 225°F), with intermittent short-term peaking up to 204°C (400°F). The major uses of Tedlar as a protective film for long term outdoor applications is on signs and exterior wall panels.

Top

11. What is Laking?
Laking is the effect of a lake or puddle in an adhesive coating. The area reflects more light due to the release liner or coating technology. Laking has no effect on the finished application.
Laking can be caused by one of two factors. 1) bad application of adhesive by the manufacturer. 2 ) films with a high (greater than 6ml) adhesive coating.

Where the adhesive ratio is high, laking can be caused when the roll laminator is heated and liquifies the adhesive, the rolls (nip point) are inconsistent and/or uneven causing the liquified adhesive to spread out unevenly.

Top

12. What is Piping?
Piping is expansion or contraction of release liner or media due to change in environmental moisture balance.

Top

13. What is Silvering?
Silvering is the speckled appearance of a laminated print or air bubbles trapped under the lamination film. Silvering may not be a permanent effect. It is usually reduced with hot or heat–assisted lamination.

Top

14. What is Telescoping?
Telescoping can be caused when a roll of material is picked up and the film slides within the roll and causes a telescope effect so that the end of the roll is no longer flush with core.

Top

15. What is Shrinkage?
Shrinkage is a condition that can occur to both Laminates and Adhesives. The root cause for this condition is derived from two culprits: excessive tension and/or too much heat applied during the application which can cause "stretching" to occur.

Once the graphic is "finished" all looks well, within a short time frame you will see that the Laminate has "shrunk" and has pulled away from the edges of the graphic, the laminate appearing to be "smaller" in size than the graphic. Adhesive "shrinkage" will also be quite noticeable, causing graphics to pull away from the edges of their substrates and in some cases causing the graphic to "pop" off of their mounting substrates.

Top

16. How do you know if your adhesive is water-based or not?
Place a laminate sample into a glass of water. The film turning cloudy after 10 minutes indicates it is water based. If the film colour remains unchanged it is likely to be solvent based.

Top

17. What is Curling?
Curling is quite easily noticeable. The print is not flat. When the image exits the back of the laminator the image will "curl" either upwards towards the top of the laminator or downwards towards the bottom of the laminator. The cause for curling is "brake" or tension applied to the roll of material. Upward curl implies too much brake on your top roll of material, Downward curl implies too much "brake" on the bottom roll of material. Reduce the amount of brake on the proper roll of material and the "curl" is reduced and eliminated.

Top

18. What is Boat waking?
This is where the output is clean in the middle but has ripples on both the left and right side.

Top

19. Why is my laminate not sticking to the image?
Several reasons could be possible a)the laminate is not compatible with the media or ink being used, b) the temperature is not hot enough, c)not enough rpessure has been applied or d) the print was not dry before lamination.

Top

20. How long will my print last if I laminate it with a UV protective laminating film?
It is very difficult to put a life span on a print due to all of the environmental factors as well as all the different types of ink and media characteristics. Generally, the color fade time can be as much as doubled by using a UV protective film.

Top

21. Can I roll up a large print if it is laminated with a pressure sensitive film? Will it "Tunnel"?
You may roll it up as long as the image is first allowed to cure for 24 hours and the inside diameter of the loosely rolled up image remains greater than 6 inches and is rolled ‘Printed Side Out’. If rolled up too tightly, separation may occur between the image and lamination creating a "tunnel".

Top

22. Are SEAL adhesives "archival"?
Although all of our adhesives have a neutral pH, they are not considered archival. The bond from our adhesives is permanent.

Top

23. What is a high temperature heat activated film and a low temperature heat activated film?
High temperature laminates will usually require roller temperatures of 210-235°F or above, while low temp films will activate at 180-205°F roller temperature.

Top

24. Can I use the least expensive heat activated film for all lamination?
No, the least expensive thermal films are usually polyester based and will not adhere to all types of medias and substrates. ‘Duratrans’ is a good example of a media that should not be laminated with this type of film.

Top

25. What is a release liner?
A release liner is a protective sheet that is covering the adhesive layer on a film product. This liner is removed and discarded while running the film through a laminator.

Top

26. What is the ‘film to adhesive ratio’ and what is its relevance?
When discussing film composition and its thickness, the industry standard is to refer to ‘film to adhesive ratio’. This ratio represents how thick the film is and how thick the adhesive is that has been applied to the film. For example, the SEALJet Guard UV Gloss 10mil film has a 7/3 film to adhesive ratio which means that the film thickness is 7mil and the adhesive on it is 3mil thick.

Thick coatings of adhesive add a slightly yellow tint to the film. Some profesional printers account for this through color correction before lamination to hit exact colors. The slight yellowing is not usually noticeable or a problem. For this reason, better quality laminates will have thick film and low adhesive ratio's to provide optimum optical clarity.

Top

27. What is a Decal?
A Decal is an image that may or may not have a laminate on the top and a backing that can be removed, revealing a sticky surface. Decaling is the process of taking a print/image and converting it to a print with a sticky backing and removable liner.

Top